Effects of different acids and etching times on the bond strength of glass fiber–reinforced composite root canal posts to composite core material

Ahmet Umut Guler, DDS, PhD/Murat Kurt, DDS, PhD/Ibrahim Duran, DDS/ Altay Uludamar, DDS, MSc, PhD/Ozgur Inan, DDS, PhD

Pages: e1-e8
PMID: 22259812

Objective: To investigate the effects of different acids and etching times on the bond strength of glass fiber–reinforced composite (FRC) posts to composite core material. Method and Materials: Twenty-six FRC posts (FRC Postec Plus) were randomly divided into 13 groups (each n = 2). One group received no surface treatment (control). The posts in the other groups were acid etched with 35% phosphoric acid and 5% and 9.6% hydrofluoric acid gel for four different etching times (30, 60, 120, and 180 seconds). A cylindric polytetrafluoroethylene mold was placed around the treated posts and filled with dual-cure composite core material (MultiCore Flow). All samples were light cured for 60 seconds. After 24 hours of water storage, the specimens were sectioned perpendicularly to the bonded interface under water cooling to obtain 2-mm post-and-core specimens. Eight specimens were made from each group. Push-out tests were performed at a crosshead speed of 0.5 mm/min using a universal testing machine. Data were analyzed by one-way ANOVA followed by the Tukey honestly significant difference test (alpha = .05). Results: The lowest bond strength was observed in the control group (12.51 megapascal [MPa]). No statistical significant difference was observed among group H5-120 (20.31 MPa), group H9-120 (20.55 MPa), or group P-180 (20.57 MPa) (P > .05). These groups demonstrated the highest bond strength values (P < .05). Conclusion: For the FRC posts, all acid-etching procedures tested showed significantly increased bond strength when compared with the control group. Acid-etching with 5% hydrofluoric acid and 9.6% hydrofluoric acid for 2 minutes and with 35% phosphoric acid for 3 minutes (groups H5-120, H9-120, and P-180, respectively) demonstrated the highest bond strength values between the FRC post and composite core material. Although the bond strength was increased by prolonged acid etching, the microstructure of the FRC posts might have been damaged. (Quintessence Int 2012;43:e1–e8

Key words: acid etching, bond strength, composite core material, etching time, FRC post, hydrofluoric acid, phosphoric acid

Full Text PDF File | Order Article

 

Get Adobe Reader
Adobe Acrobat Reader is required to view PDF files. This is a free program available from the Adobe web site.
Follow the download directions on the Adobe web site to get your copy of Adobe Acrobat Reader.
  © 2014 Quintessence Publishing Co Inc
 

Home | Subscription Services | Books | Journals | Multimedia | Events | Blog
Terms of Use | Privacy Policy | About Us | Contact Us | Advertising | Help | Sitemap | Catalog