Osteoblastic Cell Attachment to Hydroxyapatite-Coated Implant Surfaces In Vitro

Yu-Liang Chang, DDS, Clark M. Stanford, DDS, PhD, James S. Wefel, PhD, John C. Keller, PhD


PMID: 10212541

Hydroxyapatite (HA) used as a coating for implants can exhibit varying levels of interaction with the biologic environment. The crystallinity of the HA-based coating has been shown to control the rate of dissolution and appears to play a role in the initial cellular interaction with the implant surfaces. An osteoblastic cell attachment assay was employed to examine the cell attachment to untreated and pretreated (pH 5.2, 24 hours) titanium and HA coatings of low (50%), medium (75%), and high (90%) crystallinity. A slightly higher percentage of cell attachment (%CA) was found on untreated and pretreated HA surfaces as compared to the titanium surface. No significant difference could be found in the %CA between the 3 levels of crystallinity. However, higher levels of %CA were observed on pretreated HA surfaces than on untreated HA surfaces (t test, P < .05). Elevated calcium and phosphate levels in culture medium did not have any effect on cell attachment. Scanning electron microscopic examinations revealed surface degradation of the HA coating following pretreatment in the simulated inflammatory media (pH 5.2, 24 hours). The results suggest that the altered surface topography may influence the initial cell attachment to HA surfaces. (Int J Oral Maxillofac Implants 1999;14:239247) Key words: cell adhesion, crystallinity, dissolution, hydroxyapatite, osseointegration, osteoblast


Full Text PDF File | Order Article

 

 
Get Adobe Reader
Adobe Acrobat Reader is required to view PDF files. This is a free program available from the Adobe web site.
Follow the download directions on the Adobe web site to get your copy of Adobe Acrobat Reader.

 

© 2014 Quintessence Publishing Co, Inc JOMI Home
Current Issue
Ahead of Print
Archive
Author Guidelines
About
Accepted Manuscripts
Submission Form
Submit
Reprints
Permission
Advertising
Quintessence Home
Terms of Use
Privacy Policy
About Us
Contact Us
Help