Bone Response to Plasma-Sprayed Hydroxyapatite and Radiofrequency-Sputtered Calcium Phosphate Implants in Vivo

Joo L. Ong, PhD, Kazuhisa Bessho, DDS, DMSc, David L. Carnes, PhD


PMID: 12182302

Purpose: The objective of this study was to evaluate the effect of radiofrequency- (RF) sputtered calcium phosphate (CaP) coating of titanium implants on bond strength at the bone-implant interface and percent bone contact length. Materials and Methods: Cylindric sputtered CaP-coated and plasmasprayed hydroxyapatite- (HA) coated implants (4.0 mm diameter and 8 mm length) were implanted in dog mandibles. Half the sputtered CaP-coated implants were heat-treated. Results: Twelve weeks after implant placement, no statistical differences in the mean ultimate interfacial strengths were observed between as-sputtered CaP-coated, sputtered CaP-coated heat-treated, and control plasma-sprayed HAcoated implants. Histomorphometric evaluation indicated that the percent bone contact lengths for the plasma-sprayed HA-coated implants and the as-sputtered CaP-coated implants were similar and significantly greater than that for the sputtered CaP-coated heat-treated implants. Differences in the ultimate interfacial strength and percent bone contact length between different implant sites in the mandible were not observed. Discussion: The results of this study, considered together with the results of previous studies, suggest that once early osseointegration is achieved, biodegradation of the thin CaP coatings is not detrimental to bone-coating-implant fixation, and does not compromise bone responses to the coated implant surfaces. Conclusion: The interfacial strength and histomorphometric data suggest that the CaP coatings applied using the sputtering process produce bone responses similar to those of HA coatings applied using plasma spraying. (INT J ORAL MAXILLOFAC IMPLANTS 2002;17:581586)


Full Text PDF File | Order Article

 

 
Get Adobe Reader
Adobe Acrobat Reader is required to view PDF files. This is a free program available from the Adobe web site.
Follow the download directions on the Adobe web site to get your copy of Adobe Acrobat Reader.

 

© 2014 Quintessence Publishing Co, Inc JOMI Home
Current Issue
Ahead of Print
Archive
Author Guidelines
About
Accepted Manuscripts
Submission Form
Submit
Reprints
Permission
Advertising
Quintessence Home
Terms of Use
Privacy Policy
About Us
Contact Us
Help