Effects of Mechanical and Thermal Fatigue on Dental Drill Performance

Benjamin H. Harris/Sean S. Kohles, PhD


PMID: 11769832

Osseous integration of dental implants depends on the use of proper surgical technique during site preparation, including the prevention of thermal injury to the surrounding bone. Heat generation during drilling has been reported to positively correlate with the production of forces at the surgical site. In this study, peak torque and axial load levels were measured during a drilling procedure into a polymeric material simulating the human mandible. Axial rotary milling was performed using 5 different twist drill designs (3i Irrigated Tri-Spade, 3i Disposable, Nobel-Biocare, Straumann, and Lifecore) of 15 to 20 mm in length and 2 to 2.3 mm in diameter, at a free-running rotational speed of 1,500 rpm and continuous feed rate of 3.5 mm/second, to a total depth of 10.5 mm. Ten drills representing each of the 5 types (n = 50) were subjected to 30 individual drill pecks and heat-sterilized every 3 pecks to determine the effects of cyclic mechanical and thermal loading on drill performance. Normal stress ()and shear stress () were calculated from the kinetic data and drill geometries. A drill efficiency coefficient () was also calculated as the ratio of torsional resistance to translational resistance. Overall, the hypotheses of drill performance dependency on drill type as well as mechanical and thermal accumulated loading were tested and confirmed (P < .05). The 5 drill types produced a range of normal stresses (2.54 to 5.00 MPa), shear stresses (9.69 to 29.71 MPa), and efficiency (1.16 to 3.16) during repeated testing. Scanning electron microscopic images revealed minor deformations in the cutting edges of the tri-spade drills following testing. (INT J ORAL MAXILLOFAC IMPLANTS 2001;16:819826)


Full Text PDF File | Order Article

 

 
Get Adobe Reader
Adobe Acrobat Reader is required to view PDF files. This is a free program available from the Adobe web site.
Follow the download directions on the Adobe web site to get your copy of Adobe Acrobat Reader.

 

© 2014 Quintessence Publishing Co, Inc JOMI Home
Current Issue
Ahead of Print
Archive
Author Guidelines
About
Accepted Manuscripts
Submission Form
Submit
Reprints
Permission
Advertising
Quintessence Home
Terms of Use
Privacy Policy
About Us
Contact Us
Help