The Effect of Chemical and Nanotopographical Modifications on the Early Stages of Osseointegration

Luiz Meirelles, DDS, PhD/Fredrik Currie, PhD/Magnus Jacobsson, MD, PhD/Tomas Albrektsson, MD, PhD/Ann Wennerberg, DDS, PhD


PMID: 18807559

Purpose: To investigate the effect of chemically modified implants with similar microtopographies but different nanotopographies on early stages of osseointegration. Materials and Methods: Forty screw-shaped implants were placed in 10 New Zealand white rabbits. The implant surface modifications investigated in the present study were (1) blasting with TiO2 and further (2) fluoride treatment or (3) modification with nano-hydroxyapatite. Surface evaluation included topographical analyses with interferometry, morphologic analyses with scanning electron microscopy, and chemical analyses with x-ray photoelectron spectroscopy. Bone response was investigated with the removal torque test, and histologic analyses were carried out after a healing period of 4 weeks. Results: Surface roughness parameters showed a slight decrease of the average height deviation for the fluoride-treated compared to the blasted (control) and nano-hydroxyapatite implants. Scanning electron microscopic images at high magnification indicated the presence of nanostructures on the chemically modified implants. Chemical analyses revealed the presence of titanium, oxygen, carbon, and nitrogen in all implant groups. The blasted-fluoride group revealed fluoride, and the blasted-nano HA group calcium and phosphorus with simultaneous decrease of titanium and oxygen. Removal torque values revealed an increased retention for the chemically modified implants that exhibit specific nanotopography. The histologic analyses demonstrated immature bone formation in contact with the implant surface in all groups, according to the healing period of the experiment. Conclusion: Chemical modifications used in the present study were capable of producing a particular nanotopography, and together with the ions present at the implant surface, may explain the increased removal torque values after a healing period of 4 weeks. Int J Oral Maxillofac Implants 2008;23:641647

Key words: dental implants, hydroxyapatite, nanotopography, osseointegration, surface modification, titanium fluoride


Full Text PDF File | Order Article

 

 
Get Adobe Reader
Adobe Acrobat Reader is required to view PDF files. This is a free program available from the Adobe web site.
Follow the download directions on the Adobe web site to get your copy of Adobe Acrobat Reader.

 

© 2014 Quintessence Publishing Co, Inc JOMI Home
Current Issue
Ahead of Print
Archive
Author Guidelines
About
Accepted Manuscripts
Submission Form
Submit
Reprints
Permission
Advertising
Quintessence Home
Terms of Use
Privacy Policy
About Us
Contact Us
Help