A Clinical Study Assessing the Influence of Anodized Titanium and Zirconium Dioxide Abutments and Peri-implant Soft Tissue Thickness on the Optical Outcome of Implant-Supported Lithium Disilicate Single Crowns

Francisco Martínez-Rus, DDS, PhD/Marta Prieto, DDS/María P. Salido, DDS, PhD/Cristina Madrigal, DDS, PhD/Mutlu Özcan, DDS, Dr Med Dent, PhD/Guillermo Pradíes, DDS, PhD


PMID: 28095519
DOI: 10.11607/jomi.5258

Purpose: To assess the influence of anodized titanium and zirconium dioxide abutments and peri-implant soft tissue thickness on the optical outcome of implant-supported lithium disilicate single crowns. Materials and Methods: Twenty patients with a missing maxillary single incisor, canine, or first premolar received an endosseous implant after a two-stage surgery protocol. After healing and soft tissue conditioning, peri-implant soft tissues were reproduced in the impression, and the thickness was measured. Customized abutments were made of titanium, gold-anodized titanium, pink-anodized titanium, and zirconium dioxide. The definitive prosthesis was a lithium disilicate crown stratified by feldsphatic porcelain. Customized abutments were screwed (35 Ncm), and the crown was temporarily placed on the abutment with a try-in paste. Color measurements were made using a spectrophotometer. CIELab color scale was employed following the formula: ΔE = (ΔL)2 + (Δa)2 + (Δb)2. Data were analyzed using repeated-measures analysis of variance (ANOVA), Bonferroni and Pearson’s correlation tests (α = .05). Results: Abutment material type significantly affected the ΔE values at both the peri-implant soft tissue (P = .0001) and coronal level (P = .001). The lowest ΔE values were obtained with zirconia abutments at both soft tissue (6.06 ± 3.2) and coronal level (5.76 ± 2.9) compared with those of other abutments (soft tissue: 8.96 ± 3.1 to 11.56 ± 3.4; coronal: 8.66 ± 6.1 to 10.42 ± 6.3). Mean soft tissue thickness (1.63 ± 0.64 mm) affected the ΔE values at the peri-implant soft tissue level for only titanium and pink-anodized titanium abutments (P = .024 and P = .048, respectively). In all conditions, correlation coefficients between ΔE and the abutment materials were higher for titanium (r = –0.544; P = .024) and the least for zirconia (r = –0.313; P = .238) and gold-anodized titanium (r = –0.393; P = .119) abutments. Conclusion: All abutment types demonstrated noticeable color difference at both the soft tissue and coronal levels. Zirconia abutments showed the lowest ΔE values at both measurement zones. Soft tissue thickness did not affect the ΔE values at the peri-implant soft tissue level.


Full Text PDF File | Order Article

 

 
Get Adobe Reader
Adobe Acrobat Reader is required to view PDF files. This is a free program available from the Adobe web site.
Follow the download directions on the Adobe web site to get your copy of Adobe Acrobat Reader.

 

© 2017 Quintessence Publishing Co, Inc JOMI Home
Current Issue
Ahead of Print
Archive
Author Guidelines
About
Accepted Manuscripts
Submission Form
Submit
Reprints
Permission
Advertising
Quintessence Home
Terms of Use
Privacy Policy
About Us
Contact Us
Help