Home Subscription Services
 
   

 
The Journal of Adhesive Dentistry
JAD Home Page
About the Editor
Editorial Board
Submit
Author Guidelines
Submission Form
Reprints / Articles
Permissions
Advertising
Advertising
MEDLINE Search
 
 
 
 
 
FacebookTwitterYouTube
Quintessence Publishing: Journals: JAD

 

The Journal of Adhesive Dentistry

Edited by Jean-François Roulet

ISSN (print) 1461-5185 • ISSN (online) 1757-9988

Publication:

May/June 2009
Volume 11 , Issue 3



Pages: 191-198
Back
Share Abstract:

Influence of Chlorhexidine Concentration on the Durability of Etch-and-Rinse Dentin Bonds: A 12-month In Vitro Study

Breschi, Lorenzo / Cammelli, Federica / Visintini, Erika / Mazzoni, Annalisa / Vita, Francesca / Carrilho, Marcela / Cadenaro, Milena / Foulger, Stephen / Mazzotti, Giovanni / Tay, Franklin R. / Di Lenarda, Roberto / Pashley, David

Purpose: To investigate the effect of 0.2% and 2% chlorhexidine (CHX) used as a therapeutic primer on the long-term bond strengths of two etch-and-rinse adhesive systems. Materials and Methods: Adper Scotchbond 1XT (SB1) and XP-Bond (XPB) were evaluated. Etched dentin substrates were assigned to 6 treatment groups: (1) 0.2% CHX + SB1; (2) 2% CHX + SB1; (3) SB1 (control); (4) 0.2% CHX + XPB; (5) 2% CHX + XPB; (6) XPB (control). Composite buildups were made and beams prepared for microtensile bond strength testing. Beams were divided into 3 subgroups and either immediately pulled to failure or stored in artificial saliva for 6 or 12 months prior to testing. Data were evaluated with three-way ANOVA. Additional adhesive interfaces were prepared to investigate nanoleakage expression by TEM. Results: SB1 and XPB showed similar immediate bond strength values with or without CHX pretreatment (p > 0.05). After 12 months, bonds fell from 43.9 9.5 MPa to 20.1 5.4 MPa and from 39.6 9.4 MPa to 14.2 5.0 MPa in control specimens for SB1 and XPB respectively, while bond fell only from 41.9 9.6MPa to 33.2 8.3 MPa and 38.3 8.9 MPa to 26.5 10.9 (for SB1 and XPB, respectively) when 0.2% CHX was previously used. CHX concentration did not affect bond strength values (0.2% vs 2%, p > 0.05). Nanoleakage increased during aging in controls, but reduced silver deposits were found in CHX-treated specimens. Conclusion: Chlorhexidine significantly reduced the loss of bond strength seen in control bonds. Since no bacterial growth was present in the aging conditions, the results of this study suggest that endogenous factors thought to degrade the adhesive interface can be inhibited by CHX. Further in vivo trials should confirm the role of CHX in bond durability.

Keywords: chlorhexidine, dental bonding systems, hybrid layer, aging, dentin

Full Text PDF File | Order Article

 

 
  © 2014 Quintessence Publishing Co Inc
 

Home | Subscription Services | Books | Journals | Multimedia | Events | Blog
Terms of Use | Privacy Policy | About Us | Contact Us | Advertising | Help | Sitemap | Catalog