Home Subscription Services
 
   

 
The Journal of Adhesive Dentistry
JAD Home Page
About the Editor
Editorial Board
Submit
Author Guidelines
Submission Form
Reprints / Articles
Permissions
Advertising
Advertising
MEDLINE Search
 
 
 
 
 
FacebookTwitterYouTube
Quintessence Publishing: Journals: JAD

 

The Journal of Adhesive Dentistry

Edited by Jean-François Roulet

ISSN (print) 1461-5185 • ISSN (online) 1757-9988

Publication:

July/August 2013
Volume 15 , Issue 4



Pages: 369-376
PMID: 23534029
DOI: 10.3290/j.jad.a29013
Back
Share Abstract:

Effect of Different Surface Treatments on Adhesion of In-Ceram Zirconia to Enamel and Dentin Substrates

Saker, Samah / Ibrahim, Fatma / Özcan, Mutlu

Purpose: Resin bonding of In-Ceram Zirconia (ICZ) ceramics is still a challenge, especially for minimally invasive applications. This study evaluated the adhesion of ICZ to enamel and dentin after different surface treatments of the ceramic.
Materials and Methods: ICZ ceramic specimens (diameter: 6 mm; thickness: 2 mm) (N = 100) were fabricated following the manufacturer’s instructions and randomly assigned to 5 groups (n = 20), according to the surface treatment methods applied. The groups were as follows: group C: no treatment; group SB: sandblasting; group SCS-S: CoJet+silane; group SCS-P: CoJet+Alloy Primer; group GE-S: glaze+ hydrofluoric acid etching (9.6%) for 60 s+silane. Each group was randomly divided into two subgroups to be bonded to either enamel or dentin (n = 10 per group) using MDP-based resin cement (Panavia F2.0). All the specimens were subjected to thermocycling (5000x, 5°C-55°C). The specimens were mounted in a universal testing machine and tensile force was applied to the ceramic/cement interface until failure occurred (1 mm/min). After evaluating all the debonded specimens under SEM, the failure types were defined as either adhesive with no cement left on the ceramic surface (score 0) or mixed with less than 1/2 of the cement left adhered to the surface with no cohesive failure of the substrate (score 1). The data were statistically evaluated using 2-way ANOVA and Tukey’s tests (α = 0.05).
Results: The highest tensile bond strength for the enamel surfaces was obtained in group GE-S (18.1 ± 2 MPa) and the lowest in group SB (7.1 ± 1.4 MPa). Regarding dentin, group CSC-P showed the highest (12 ± 1.3 MPa) and SB the lowest tensile bond strength (5.7 ± 0.4 MPa). Groups SB, CSC-S, CSC-P, and GE-S did not show significant differences between the different surface treatments on either enamel or dentin surfaces (p < 0.05, p < 0.001, respectively). Groups CSC-P and GE-S presented similar bond strength for both the enamel and dentin substrates (p < 0.8 and p < 0.9), respectively. While on enamel substrates, exclusively adhesive failures from ICZ (score 0) were found, on dentin exclusively mixed failures were observed (score 1).
Conclusion: Adhesion of ICZ to both enamel and dentin can be improved when ceramics are glazed, etched, and silanized, or sandblasted, primed, and cemented with an MDP-based cement.

Keywords: adhesion, adhesive cement, alloy primer, glaze, In-Ceram Zirconia, surface conditioning, tensile bond strength

Full Text PDF File | Order Article

 

 
  © 2014 Quintessence Publishing Co Inc
 

Home | Subscription Services | Books | Journals | Multimedia | Events | Blog
Terms of Use | Privacy Policy | About Us | Contact Us | Advertising | Help | Sitemap | Catalog