The International Journal of Prosthodontics

Edited by George A. Zarb, BChD, DDS, MS, MS, FRCD(C)

ISSN 0893-2174

Publication:
May/June 1994
Volume 7 , Issue 3

Back
Share Abstract:

Fatigue Characteristics of a High-Strength Porcelain

Myers/Ergel/Fairhurst/Ringle

Pages: 253-257
PMID: 7916891

The purpose of this study was to determine stress corrosion fatigue characteristics of Optec-hsp porcelain. Disks (1 mm thick and 12 mm in diameter) were prepared according to the manufacturer’s firing recommendations. Samples were subjected to dynamic loading at multiple constant stressing rates. Dynamic fatigue was measured using a biaxial flexural strength test in a circulating bath. Inert strength was determined in a moisture-free environment. The mean fracture strength for the dry (moisture-free) samples was 167.9 MPa. Linear regression analysis of log fracture strengths vs log time to failure was performed to obtain fatigue parameters. For Optec, the n-value was 26 (SE 1.9) and sigma f0 was 91.3 MPa (SE 1.2 MPa).

Full Text PDF File | Order Article

 

 
Get Adobe Reader
Adobe Acrobat Reader is required to view PDF files. This is a free program available from the Adobe web site.
Follow the download directions on the Adobe web site to get your copy of Adobe Acrobat Reader.
  © 2014 Quintessence Publishing Co Inc
 

Home | Subscription Services | Books | Journals | Multimedia | Events | Blog
Terms of Use | Privacy Policy | About Us | Contact Us | Advertising | Help | Sitemap | Catalog