Tensile Bond Strength of Two Ceramic and Three Resin Composite Inlay Materials Placed Using a Resin Luting Agent


Pages: 233-238
PMID: 10348591

The tensile bond strength ofinlay materials to dentin was evaluated. Five materials, two direct resin composite inlay products, one hybrid resin composite, a preformed ceramic block, and a conventional porcelain material were bonded to bovine dentin and bonded together using a dual-polymerizing resin luting agent. Specimens were tested with and without thermocycling. Some bar-to-bar bonding groups fractured through the bar. Significantly higher (P<.05) bar-to-bar bonds were recorded than the bar-dentin bonds, irrespective of the inlay materials. VitaDur N Showed the lowest bar-to-bar failure values (7.6 MPa) compared to the four other inlay materials (14.4 MPa to 22.2 MPa), but had the highest dentin bond strength (4.5 MPa). Unexpectedly, thermal loading increased the bond strength to bovine dentin, although this was only statistically significant for VitaDur N. The dentin bond strength of Charisma (1.4 MPa) was inferior (P<.02) to all othe materials (2.6 MPa to 4.5 MPa) when thermocycled before testing.

Full Text PDF File | Order Article


Get Adobe Reader
Adobe Acrobat Reader is required to view PDF files. This is a free program available from the Adobe web site.
Follow the download directions on the Adobe web site to get your copy of Adobe Acrobat Reader.
  © 2017 Quintessence Publishing Co Inc

Home | Subscription Services | Books | Journals | Multimedia | Events | Blog
Terms of Use | Privacy Policy | About Us | Contact Us | Advertising | Help | Sitemap | Catalog